Everything you need to know about BauBuche – from A for applications to V for vapour barrier.
Everything you need to know about BauBuche – from A for applications to V for vapour barrier.
The veneers are dried to 2 % - 3 % timber moisture. Then they are conditioned to approx. 5 % - 6 % timber moisture. Applying the adhesive adds moisture, which pushes the moisture level of the final product back up to approx. 7 %.
The compressive strength of BauBuche is 20 % higher in service class 1 than in service class 2. Service class 1 is defined by a wood moisture corresponding to a temperature of 20 °C and a relative humidity which only exceeds 65 % for a few weeks a year. This gives wood moistures of not more than 12 %. Service class 2 is defined by a wood moisture corresponding to a temperature of 20 °C and a relative air humidity which only exceeds a value of 85 % for a few weeks a year, resulting in wood moistures of up to 20 %. The compressive strength values stated in our approvals refer to the already reduced values applicable in service class 2. An increase of 20 % for applications in service class 1 is permitted and is described both in the approvals and in the design manual.
Like spruce, beechwood will grey slightly in both interior and exterior use due to UV light, unless it is protected. The use of BauBuche is only permitted in roofed areas (service classes 1 & 2). BauBuche must not be exposed directly to weather (service class 3).
BauBuche can be impregnated. Over the next few months, impregnation plants will conduct tests to establish which impregnation agents are effective and also economic.
In this respect BauBuche is similar to solid beech wood. BauBuche is approved for use in service classes 1 and 2. In these applications, beech is only attacked by termites (this is possible in Australia, for example). Protection of finished BauBuche is difficult as the glued joints make it difficult to apply biocide reliably. Pollmeier is working on a method of applying biocide on request during the manufacture of BauBuche.
The strength of BauBuche is not affected as a result of brief exposure to the elements during assembly. BauBuche will, however, swell and stains may form. If brief exposure to the elements cannot be ruled out during transport and assembly, we recommend the use of a protective varnish, e.g., BauBuche varnish, which can be purchased from Koch und Schulte GmbH & Co.KG, 57645 Nister, www.kochundschulte.de
As a stiffening board we exclusively recommend BauBuche Q Board. The diaphragm action (2-axis load-bearing effect) which is required for a stiffening board is achieved by the veneers, up to 15 % of which run perpendicular to the main load-bearing direction.
Essentially, there is always a degree of deflection caused by the weight of the components, but it is very small, and has to be calculated. It can be counteracted by giving the beam a camber.
Offcuts can be burnt as fuel, provided that temperatures above 850 °C are guaranteed. BauBuche offcuts can also be used in the production of particleboard.
All standard varnish systems that are suitable for solid beech wood can be used for treating the surface. For BauBuche flooring, we use a varnish system from Osmo, which is not suitable for application at the construction site.
The same occupational safety requirements apply when sanding BauBuche as with solid beech wood.
In principle the same connections can be used for BauBuche as for conventional glued laminated timber. However, given the high density, a few special features must be observed. For precise information on design and calculation with BauBuche as well as structural analysis of connections, please refer to our design manual.
This is possible with the EGO system from Bucher. For more details see Bucher Treppen. This system is preferred by our Treppenmeister partner companies, who offer project-specific technical advice.
Yes, the approval / manufacturing standard allows for subsequent planing and sanding, provided that a rectangular cross-section is maintained and the girder height remains between 80 and 2500 mm.
Yes, BauBuche flooring with a thickness of 14 mm is ideal for use with underfloor heating. The thermal conductivity of our flooring is 0.134 W/(mK). The thickness divided by the thermal conductivity results in the thermal insulation resistance which must not be greater than 0.15 m²K/W. With our BauBuche flooring the thermal insulation resistance is around 0.11 m²K/W and thus suitable for underfloor heating.
Phenolic resin adhesive is used in the production of laminated veneer lumber.
It offers good economy, high strength, is water-resistant and, most importantly, no formaldehyde is released subsequently. In addition, decades of experience and countless research projects mean that everything is known about this adhesive! It is supplied by Dynea.
Yes, a camber of up to 15 cm is possible.
The current national technical approval covers beams up to the following dimensions: max. length = 35 m; max. width = 300 mm; max. cross-sectional height = 600 mm. With a special approval based on an expert report from MPA Stuttgart, today we can offer beams with the following dimensions: max. length = 35 m; max. width = 300 mm; max. cross-sectional height = 1360 mm. The enhancement of the German Technical Approval for section heights up to 2500mm is in process and expected to be finished in spring 2018. Pollmeier produces beams of 18m length maximum, lengths up to 25m are available on request until end of 2018.
The use of joints means there is no defined upper limit for the length of trusses. The maximum dimensions depend on the structural conditions, including the loads. The higher strength of BauBuche allows considerably larger spans to be planned than with frameworks made of conventional glued laminated timber.
The maximum width is 680 mm, which is the maximum cutting width of the horizontal block band sawing machine. BauBuche Panel boards can be machined like solid wood and glued together to give larger board lengths.
The thermal conductivity is 0.17 W/mK.
The heat storage capacity / thermal capacity of BauBuche is 1600 J/kg K
The mean value is the calculated (arithmetic) average of all the values measured. The characteristic value is determined in accordance with EN14374, and is the 5% quantile of all the measured values. This means that 95% of the measured values are higher than the characteristic value, which is used in the structural analyses. This ensures a large safety margin in order to avoid any risk when the product is used in construction.
The diffusion resistance of BauBuche has not yet been calculated. This value can be derived from heavy plywood and is around µ = 150 - 250. Therefore, BauBuche can be used as a vapour check, but a vapour barrier cannot be created with BauBuche.
The screw withdrawal resistance depends on the screw dimensions, screw-in angle and the density of the timber. The high density of BauBuche gives a greater screw withdrawal resistance than for softwood products. The calculation is regulated by the German National Technical Approval 9.1-838, which stipulates that the equations for solid wood are to be used for the calculation. The calculation formulas can be found in DIN EN 1995-1-1 (8.38); Eurocode 5.
Laminated veneer lumber is homogenised by the production process. The cross-sectional changes of BauBuche S are thus less pronounced than with solid wood. Nevertheless, the major difference between the length change along and across the grain still remains. The use of BauBuche Q with veneer layers arranged crosswise results in a "barrier effect" and thus reduced deformation at board level. The values are similar to the value in the longitudinal direction.